제품 상세 정보:
|
| 상품 이름: | 폴리에스테르 주입된 단열재 바인딩테이프 | Thicknee: | 0.3mm |
|---|---|---|---|
| 열 종류: | H | 하소에 있는 체중 감소: | 27% |
| 가용성 수지 내용: | 90% 이상 | 병을 고치는 것 전에 인장 강도: | 1000년 N/cm 보다 더 |
| 저장 시간: | 6Months | 재료: | 연속적이거나 휘어지거나 풀린 E-유리 방사 |
| 하이 라이트: | E Glass Fiberglass Fabric Tape,Armatures Polyester Resin Fiberglass Fabric Tape,0.3mm Fiberglass Fabric Tape |
||
0.3mm Thickness Insulation Binding Tape Polyester Resin Impregnated Fiberglass Web Banding Tape
1. Introduction:
Polyglass banding tapes consists of high-strength glass yarns laid parallel, impregnated with special high-temperature thermosetting polyester resin. During cure, the resin flows and fills the voids and air spaces to produce a homogeneous laminate with a smooth resin surface.
2. Specification
Type |
(mm) Thickness |
(mm) Tolerance |
(mm) Width |
(mm) Tolerance |
Put up |
|
H200
|
0.20 | ±0.03 | 10 | ±1 | pancake or spool |
| 15 | ±1.5 | ||||
| 0.30 | ±0.03 | ||||
| 20.25.30.50.60 | ±2 |
3. Polyester Resin Fiberglass Banding Tape Transportation
Banding tape requires special and rapid transportation arrangements. Mutual consultation is suggested for appropriateness depending on the transit period, available modes, handling, etc. Considering the sensitivity of banding tape, the buyer needs to quickly take delivery of the consignment and store it suitably
4. Storage stability
The banding tape should be stored in a low temperature environment. When using, the tape should be restored to the surrounding environment. Outside the use time, it is best to put it in a plastic cover and seal it to keep it clean and prevent moisture from condensing on the product at low temperatures.
5. Properties
Item |
Unit |
Figure |
||
Type |
— | H200 | F150- | |
Thermal class |
— | H(200℃) | F(155℃) | |
Volatile content |
% | ≤2 | ||
Loss of weight at calcination |
% | 26±2 | ||
Soluble resin content |
% | ≥90 | ||
Tensile strength before curing |
N/cm | 0.20mm | ≥1200 | ≥1000 |
| 0.30mm | ≥2000 | ≥1500 | ||
Maximum pull while banding |
N/cm | 0.20mm | ≥600 | ≥500 |
| 0.30mm | ≥1000 | ≥800 | ||
Tensile strength of ringlike sample at room temperature after curing |
Mpa | 20℃ | ||
| ≥1000 | ≥900 | |||
Tensile strength of ringlike sample at working temperature after curing |
Mpa | 200℃ | 155℃ | |
| ≥700 | ≥560 | |||
Proof tracking index |
V | ≥500 | ||
Arc resistance |
S | ≥160 | ||
Dielectric strength |
KV/mm | ≥12 | ||
Thermosetting |
— | OK | ||
Loss of tensile strength after soaked in oil |
% | ≤10 | ||
6. Features:
Thermal class F and thermal class H banding tape
Banding tape is available in thermal class F (155°C) and thermal class H (200ºC).
7. Application fields:
As a winding restraint on traction armatures, generators, other rotating machines and transformer cores
Applications where high tensile strength and insulating properties of the product can be made use of
Rotor banding Large-transformer banding Transformer banding